Synthesis, optoelectronic properties, and charge carrier dynamics of colloidal quasi-two-dimensional Cs3Bi2I9 perovskite nanosheets

Back to all publications

Publication date
DOI http://dx.doi.org/10.1039/d2nr06048e
Reference S. Ghimire, C. Rehhagen, S. Fiedler, U. Parekh, R. Lesyuk, S. Lochbrunner and C. Klinke, Synthesis, optoelectronic properties, and charge carrier dynamics of colloidal quasi-two-dimensional Cs3Bi2I9 perovskite nanosheets, Nanoscale 15, (5), 2096-2105 (2023)

Non-toxicity and stability make two-dimensional (2D) bismuth halide perovskites better alternatives to lead-based ones for optoelectronic applications and catalysis. In this work, we synthesize sub-micron size colloidal quasi-2D Cs3Bi2I9 perovskite nanosheets and study their generation and relaxation of charge carriers. Steady-state absorption spectroscopy reveals an indirect bandgap of 2.07 eV, which is supported by the band structure calculated using density functional theory. The nanosheets show no detectable photoluminescence at room temperature at near bandgap excitation which is attributed to the indirect bandgap. However, cathodoluminescence spanning a broad range from 500 nm to 750 nm with an asymmetric and Stokes-shifted emission is observed, indicating the phonon- and trap-assisted recombination of charge carriers. We study the ultrafast charge carrier dynamics in Cs3Bi2I9 nanosheets using femtosecond transient absorption spectroscopy. The samples are excited with photon energies higher than their bandgap, and the results are interpreted in terms of hot carrier generation (30 ps). Further, a relatively slow relaxation of excitons (≳3 ns) at the band edge suggests the formation of stable polarons which decay nonradiatively by releasing phonons.