Accelerated Hot-Carrier Cooling in MAPbI3 Perovskite by Pressure-Induced Lattice Compression

Back to all publications

Publication date
DOI http://dx.doi.org/10.1021/acs.jpclett.1c00676
Reference L.A. Muscarella, E.M. Hutter, J.M. Frost, G.G. Grimaldi, J. Versluis, H.J. Bakker and B. Ehrler, Accelerated Hot-Carrier Cooling in MAPbI3 Perovskite by Pressure-Induced Lattice Compression, J. Phys. Chem. Lett. 12, 17: 4118-4124 (2021)
Groups Hybrid Solar Cells, Ultrafast Spectroscopy

Hot-carrier cooling (HCC) in metal halide perovskites above the Mott transition is significantly slower than in conventional semiconductors. This effect is commonly attributed to a hot-phonon bottleneck, but the influence of the lattice properties on the HCC behavior is poorly understood. Using pressure-dependent transient absorption spectroscopy, we find that at an excitation density below the Mott transition, pressure does not affect the HCC. On the contrary, above the Mott transition, HCC in methylammonium lead iodide is around 2–3 times faster at 0.3 GPa than at ambient pressure. Our electron–phonon coupling calculations reveal ∼2-fold stronger electron–phonon coupling for the inorganic cage mode at 0.3 GPa. However, our experiments reveal that pressure promotes faster HCC only above the Mott transition. Altogether, these findings suggest a change in the nature of excited carriers above the Mott transition threshold, providing insights into the electronic behavior of devices operating at such high charge-carrier densities.